Pengaruh Rasio Aktivator Terhadap Sifat Mortar Geopolimer Dengan Metode Pencampuran Kering
DOI:
https://doi.org/10.31004/koloni.v5i3.1385Keywords:
geopolymer mortar, fly ash, activator ratio, setting time, compressive strength.Abstract
The use of Portland cement as a binder results in high carbon emissions, making it necessary to find more environmentally friendly alternative materials. Fly ash-based geopolymer mortar can serve as an alternative, with the ratio of NaOH to Na₂SiO₃ activators being one of the factors influencing the mortar’s properties. This study aims to analyze the effect of the activator ratio on the setting time of geopolymer cement paste and the compressive strength of geopolymer mortar using the dry-mixing method. The study was conducted as a quantitative experiment using four variations of the NaOH:Na₂SiO₃ ratio: 0.5:2.5, 1:2.5, 1.5:2.5, and 2:2.5. Setting time was tested using a Vicat needle, while compressive strength was tested at 7, 14, and 28 days. The results showed that the higher the NaOH-to-Na₂SiO₃ ratio, the faster the setting time. Variation V1 yielded an initial setting time of 120 minutes and a final setting time of 165 minutes, while V4 yielded 75 minutes and 120 minutes, respectively. All variations exhibited an increase in compressive strength as the curing age increased. Variation V3, with a NaOH:Na₂SiO₃ ratio of 1.5:2.5, produced the highest compressive strength: 13.9 MPa at 7 days, 14.8 MPa at 14 days, and 19.7 MPa at 28 days. Thus, V3 represents the optimal activator ratio in this study.
References
SNI-03-1968-1990, (1990). Metode Pengujian Analisis Saringan Agregat Halus dan Kasar.
SNI-03-4428-1997, (n.d.). Metode Pengujian Agregat Halus Atau Pasir Yang Mengandung Bahan Plastik Dengan Cara Setara Pasir.
SNI-03-4804-1998, (n.d.). Metode Pengujian Berat Isi dan Rongga udara dalam agregat.
SNI 1970:2008, (2008). Cara Uji Berat Jenis dan Penyerapan Air Agregat Halus.
Anugrah, D. A., & Wardhono, A. (2018). Pengaruh Variasi Naoh Terhadap Na2sio3 Terhadap Kuat Tekan Dry Geopolymer Mortar Metode Dry Mixing Pada Kondisi Rasio Abu Terbang Terhadap Aktivator 4:1 Terhadap Aktivator 4:1. 1–9.
ASTM C191-01a, (2002). Standard Test Methods for Time of Setting of Hydraulic by Vicat Needle.
Davidovits, J. (1991). Geopolymers: inorganic polymeric new materials. Journal of Thermal Analysis and Calorimetry, 37(8), 1633–1656.
Fajrin, J., Fattaah, M. A. Al, & Hariyadi. (2025). Sifat Fisik Dan Mekanik Mortar Geopolimer Berbahan Dasar Kapur Kerang Dan Abu Terbang. 1(1), 1–9.
Fauzi, A., Keliat, A. M., Majuar, E., Hajani, C. N., Mahyar, H., & Fahmi, M. (2021). Pengaruh Penggunaan Fly Ash PLTU Pangkalan Susu Terhadap Kuat Tekan Mortar Geopolimer. 5(1), 71–76.
Firdaus, & Putri, G. M. (2024). Pemanfaatan Abu Sekam Padi sebagai Bahan Pengganti Water Glass dalam Pembuatan Mortar Geopolimer Campuran Kering. 7(1), 100–112.
Fitriananda, Estetika Wardhono, A. (2022). Pengaruh Kepekatan Larutan Aktivator Terhadap Kuat Tekan Geopolymer Mortar Berbahan Dasar Abu Terbang Dan Naoh 12 Molar Pada Kondisi Ss/Sh 2.0 Dan 4.0.
Islami, M. N., & others. (2019). Pengaruh Konsentrasi Aktivator Dan Zat Additive Terhadap Setting Time Dan Kuat Tekan Beton Geopolimer. Universitas Internasional Semen Indonesia.
Khafid, M., Waliyyuddin, S., Rochman, T., & Suryadi, A. (2024). Mortar Geopolimer Mutu Tinggi Berbasis Fly Ash Dan Silica Fume : Aplikasinya Terhadap Kuat Tekan Dan Kuat Lentur. 5(September), 140–143.
Kuniawati, S., Wahyuni, A. S., Gunawan, A., Islam, M., & Afrizal, Y. (2023). Pengaruh Penggunaan Fly Ash Pada Kuat Tekan Beton Geopolimer Dengan Aktivator Natrium Hidroksida (NaOH) DAN Natrium Silikat (Na2SiO3). 17(1), 7–15.
Maryenttry, E., Firdaus, & Prawira, W. Y. (2024). Pengaruh Penambahan Kapur Pada Semen Geopolimer Terhadap Mortar Geopolimer. 7(1), 127–131.
Priastiwi, Y. A., Hidayat, A., Husna, K., & Putriagsari, F. N. (2023). Studi Perbandingan Sifat Mekanik Mortar PPC dan Mortar Geopolimer dengan Aktivator NaOH pada Rendaman Air Laut. 29(1), 40–50. https://doi.org/10.14710/mkts.v29i1.54344
Salwan, A. A., Rizal, F., & Miswar, K. (2021). Analisa Kuat Tekan Mortar Geopolimer Berbasis Fly Ash Nagan Raya Dengan Metode Dry Mix. 5(1), 40–45.
Saputra, K., Mulyati, E., & Firdaus. (2024). Pengaruh Subsitusi Ampas Tebu Pada Fly Ash Terhadap Kuat Tekan Mortar Geopolimer. 10(2), 115–123.
SNI-03-6825. (2002). Metode pengujian kekuatan tekan mortar semen Portland untuk pekerjaan sipil.
Solikin, M. (2021). Analisis Pemakaian Kombinasi Fly Ash Tipe F Dan Slag 1:1 Pada Beton Geopolymer Dengan Na2sio3 Dan Naoh Sebagai Alkali Aktivator: Sebuah Kajian Literatur. 14(1), 13–20.
Yasin, A. K. (2017). Rekayasa Beton Geopolimer Berbasis Fly Ash.
Downloads
Published
How to Cite
Issue
Section
License
Copyright (c) 2026 Sonia Sonia, Firdaus Firdaus, Leon A. Abdillah
This work is licensed under a Creative Commons Attribution-ShareAlike 4.0 International License.